Specimen lot ID,"SG300-ARL-2012-RT-16"
Material ID,"SG300-ARL"
Operator,"SEAP Student 2"
Basis testing standard,"ASTM D 1002 "
Crosshead speed,"1.27000",mm/min
Data Contact,"ARL POC 1"
Data Contact e-mail,"xxx.x.xxx@us.army.mil"
Data Contact Phone,"410 306 xxxx"
Data Contact (alternative),"ARL POC 2"
Data Contact (alternative) e-mail,"yyy.y.yyy@us.army.mil"
Data Contact (alternative) Phone,"410 306 yyyy"
Testing facility,"Weapons and Materials Research Directorate"
Testing organization,"U.S. Army Research Laboratory"
Address,"RDRL-WMM-C"
Address line 2,"APG, MD 21005-5069"
Model,"Instron Model 1125"
Load cell calibration date,"1/18/2011"
Date of sample preparation,"06/25/2012"
Date test performed,"06/29/2012"
Date test performed (end, if different),"06/29/2012"
Method description,"ASTM D 1002 
Single Lap Joint Tension Test
Author of method: US Army Research Laboratory
Date edited: 8/31/2011"
Number of specimens in sample,5
System of units,All
Changes to Lap Shear Panel Preparations,"Al panels, surfaces were wiped down with acetone before adhesive application and air dried."
Standard processing and test deviations,"2024 T3 Al Fillet: YES"
Type of silane treatment,<None>
Lap Shear joint substrate aluminum grade,other
Load Cell,25 KN (5K lbf)
Sample conditioning,Dry
Target test temperature,25°C (77°F)
Adhesive Preparation,OTHER
Mixing to Applied Pressure Time (min),"0.00000"
Cure Cycle,"24hrs @ RT then placed in an oven @ 60C for 3hrs. Panels placed in hot preheated oven and a single lead weight was placed on top plate to maintian a uniform pressure and bondline. At conclusion of 3hr cycle, samples allowed to slowcool to RT overnight with oven door closed to minimize residual bonding stress."
Material Classification,Acrylic/Acrylate
Humidity at sample preparation,"52.00000"
Temperature at sample preparation (C),"72.90000"
Pressure during Curing (Mpa),"0.03000"
Data Source,Government

Results Table 1
,Maximum Load,Extension at Maximum Load
,(N),(mm)
1,"4,329.10584","2.27379"
2,"4,345.41665","2.27379"
3,"4,205.24031","2.32165"
4,"4,280.19240","2.27407"
5,"4,335.52004","2.27379"