Lattice Parameters, Densities, Expansion Coefficients and Perfection of Structure of Cu and Cu-In alpha Phase
(1969-04-08)Spectroscopically pure Cu has a lattice parameter a25 = 3.61491 Å (corrected for refraction), and a thermal expansion coefficient [alpha] = 14.87 × 10-6°C-1 between 15 and 55°C. The measured density d25 is 8.9314 ± 0.0002 ... -
Materials Informatics Approach to Material Extrusion Additive Manufacturing
Processing-structure-property relationships in material extrusion additive manufacturing are complex, non-linear, and poorly understood. In this work, we designed an informatics workflow for the collection of high pedigree ... -
Measurement of Equilibrium Concentrations of Vacancies in Copper
(2014-07-02)The net added fraction of thermally-generated atomic sites, ΔNN, has been measured, during equilibrium heating to near the melting point, in a coarse-grained copper bar of 99.999% purity. The linear thermal expansion, ΔLL, ... -
Measurment of Equilibrium Concentrations in Aluminum
(1959-07-31)Measurements of change in length and change in lattice parameter were made at identical temperatures on 99.995% aluminum in the temperature range 229 to 656°C. Length changes, ΔL, were measured on an unconstrained horizontal ... -
Mg Self-Diffusion
(2013-08-09)The self-diffusion of magnesium along the c-axis and perpendicular to it has been investigated in the temperature range from 500 to 630 C. -
Mg Self-Diffusion
(2013-08-09)The determination of the self-diffusion coefficient of magnesium has been made possible recently by discovery of a radioactive isotope, Mg-28 having a half-life of 21.3 hr, and subject to manufacture in useful quantity. -
Mg Self-Diffusion Pavlinov 1968
(2013-08-29)It is found that the parameters of self-diffusion and carbon diffusion in calcium are in good agreement with the general regularities for self-diffusion in pure metals and interstitial impurity diffusion in metals with a ... -
Mg-Al Interdiffusion and Phase Growth Kinetics
(2013-05-07)Binary interdiffusion data as functions of composition in the Mg-Al system are essential in modeling kinetics of phase transformations in multicomponent Mg and Al alloys. Interdiffusion and phase growth kinetics were studied ... -
Multivariate Analysis of High Through-Put Adhesively Bonded Single Lap Joints: Experimental and Work Flow Protocols - Analysis results
(2016-03-24)Formatted categorical and numerical variables for multivariate analysis -
Multivariate Analysis of High Through-Put Adhesively Bonded Single Lap Joints: Experimental and Work Flow Protocols - Failure surface images
(2016-03-23)Mode-of-failure images and surveys, 300 dots per inch (dpi) resolution, Tagged Image File Format (TIFF) -
Multivariate Analysis of High Through-Put Adhesively Bonded Single Lap Joints: Experimental and Work Flow Protocols - Load vs. displacement data
(2016-03-24)Raw and analyzed load versus displacement data, including semi-automated routines for maximum strength, displacement, and area under the curve -
Multivariate Analysis of High Through-Put Adhesively Bonded Single Lap Joints: Experimental and Work Flow Protocols - Supplementary data
(2016-03-24)Supporting technical data sheets, MSDS, surface pretreatment and bonding processes, travel sheets, and mode-of-failure surveys -
Multivariate Analysis of High Through-Put Adhesively Bonded Single Lap Joints: Experimental and Work Flow Protocols – Constitutive mechanical properties
(2018-05-31)Tensile stress-strain mechanical test results and analysis for the adhesives and aluminum adherend. -
Multivariate Analysis of High Through-Put Adhesively Bonded Single Lap Joints: Experimental and Workflow Protocols - Full report
(2016-06-07)An adhesively bonded single lap joint was used to study the effects of coupon thickness, bondline thickness, surface preparation, presence of an overflow fillet, and adhesive type. Gains in the Education of Mathematics and ... -
Nature of Long-Range Order in Cu3+xAu1-x
(2003-11-17)The diffuse scattering and intensities of Bragg peaks from single crystals of Cu77Au23 and Cu78Au22 have been studied for various degrees of long‐range order. The results indicate that the excess Cu atoms, replacing Au in ... -
Ni Self-Diffusion
(2013-06-26)Self-diffusion in nickel single crystals is measured between 813 and 1193 K using ion-beam sputtering as a microsectioning technique. Gaussian activity-depth profiles are observed over about three orders of magnitude in ... -
On the Anomalous Self-Diffusion in B.C.C. Titanium
(2013-07-03)Self-diffusion of the Ti44 is measured in Beta-Titanium under UHV conditions int eh whole range of existence of the bcc phase. The Arrhenius plot shows a strong upward curvature in agreement with previous investigations ... -
Phase equilibria and thermodynamic calculation of the CoeTa binary system
(2014-09-29)Experimental investigation and thermodynamic evaluation of the CoeTa binary phase diagram was carried out. Equilibrium compositions obtained in two-phase alloys and diffusion couples were measured by electron probe ... -
Raw and Processed Data to Generate Three-Dimensional Grain Map of Open-Cell Aluminum Foam
(2018-08-03)A three-dimensional grain map of an investment-cast, open-cell, aluminum foam is generated using a combination of experimentally derived and synthetically derived data. Specifically, the experimental data are derived from ...