Now showing items 1-8 of 8
Multivariate Analysis of High Through-Put Adhesively Bonded Single Lap Joints: Experimental and Work Flow Protocols - Analysis results
(2016-03-24)
Formatted categorical and numerical variables for multivariate analysis
Multivariate Analysis of High Through-Put Adhesively Bonded Single Lap Joints: Experimental and Work Flow Protocols - Supplementary data
(2016-03-24)
Supporting technical data sheets, MSDS, surface pretreatment and bonding processes, travel sheets, and mode-of-failure surveys
Multivariate Analysis of High Through-Put Adhesively Bonded Single Lap Joints: Experimental and Work Flow Protocols - Failure surface images
(2016-03-23)
Mode-of-failure images and surveys, 300 dots per inch (dpi) resolution, Tagged Image File Format (TIFF)
Multivariate Analysis of High Through-Put Adhesively Bonded Single Lap Joints: Experimental and Work Flow Protocols - Load vs. displacement data
(2016-03-24)
Raw and analyzed load versus displacement data, including semi-automated routines for maximum strength, displacement, and area under the curve
Multivariate Analysis of High Through-Put Adhesively Bonded Single Lap Joints: Experimental and Workflow Protocols - Full report
(2016-06-07)
An adhesively bonded single lap joint was used to study the effects of coupon thickness, bondline thickness, surface preparation, presence of an overflow fillet, and adhesive type. Gains in the Education of Mathematics and ...
Co-Al-W Diffusion Mobilities
(2016-04)
Diffusion couple experiments between various Co-rich face centered cubic (FCC) alloys in the Co-W-Al ternary system have been conducted at 900 °C and 1000 °C. Diffusion coefficients have been extracted for the Co-W binary ...
GaN nanowire image acquired by near-field scanning microwave microscopy
(2016-07-27)
I have posted ascii file versions of image files corresponding to near-field scanning microwave microscopy (NSSM) images of a GaN nanowire. One image (fig5a.txt) corresponds to the raw image which is shown in Figure 5a ...
In-Situ High-Throughput Synchrotron Diffraction Data of Multiple Principle Component Alloy Thin Films
(2016-08-05)
This data set is composed of a set of labeled synchrotron diffraction data taken at beamline 1-5 at SLAC on (Al1−x−yCuxMoy)FeNiTiVZr composition spread samples. The data were taken to test the relative importance of ...