Binary interdiffusion data as functions of composition in the Mg-Al system are essential in modeling kinetics of phase transformations in multicomponent Mg and Al alloys. Interdiffusion and phase growth kinetics were studied ...

It has been observed that the metals which exhibit anomalous diffusion behaviour are all allotropic in nature. A hypothesis to rationalise this interrationship between the diffusion behaviour and the phase transformation ...

Bulk Self-Diffusion was measure in alpha-Titanium single crystals between 776 and 1132 K using the radiotracer Ti44 and ion beam sputtering for profile sectioning.

Self diffusion of Cr-51 in pure chromium, Cr +20 wt% Ni, Cr +44wt% Ni, and Cr +65%wt Ni has been measured over the temperature ranges of 1000 to 1900, 1000 to 1525, and 900 to 1350 degrees C, respectively.

Solid-to-solid diffusion couples were assembled and annealed to examine the diffusion between pure Mg (99.96 pct) and Al (99.999 pct). Diffusion anneals were carried out at 573 K, 623 K and 673 K (300 C, 350 C and 400 C) ...

Self-diffusion in chromium single crystals has been measured over the temperature range 1073 to 1446 K. These data, when combined with earlier measurements from this laboratory over the. range 1370—2090 K, yield a plot ...

The diffusion of Ti44 and V48 in the b.c.c. phase of iodide titanium has been studied over the temperature range 909-1550°C. The resulting Arrhenius-type plots show curvature with the apparent activation energies and ...

Self-diffusion in nickel single crystals is measured between 813 and 1193 K using ion-beam sputtering as a microsectioning technique. Gaussian activity-depth profiles are observed over about three orders of magnitude in ...

The self-diffusion of magnesium along the c-axis and perpendicular to it has been investigated in the temperature range from 500 to 630 C.