Al-Co-W 900C Phase Equilibria Data
Phase equilibria at 900 °C in the Co-rich Co-Al-W ternary system are investigated through isothermal annealing of six alloy compositions for times up to 8000 h. The volume fraction of the L12-γ′ phase co-existing with ...
Al-Co, Co-Fe Diffusion Mobilities, Ni/Rene88, IN718/Rene88
A multicomponent diffusion mobility database for the Ni-rich fcc phase [2002Cam] is evaluated by comparing diffusion simulations to two experimental multicomponent Ni-base superalloy diffusion couples: Ni/Rene´-88 and ...
Co-Al-W Diffusion Mobilities
Diffusion couple experiments between various Co-rich face centered cubic (FCC) alloys in the Co-W-Al ternary system have been conducted at 900 °C and 1000 °C. Diffusion coefficients have been extracted for the Co-W binary ...
Interdiffusion in the Ni-Re System: Evaluation of Uncertainties
Diffusion couple experiments between Ni and Re at 1200 and 1350 °C were performed. These experiments established the limits of the two-phase FCC + HCP region. No intermediate phase was observed at these temperatures. ...
Experimental Investigation and Thermodynamic Modeling of the Co-Rich Region in the Co-Al-Ni-W Quaternary System
The stabilities of the γ-(Co), γ′-Co3(Al,W), μ-Co7W6, β-CoAl and α-(W) phases in the Co-Al-W and Ni-Al-W ternary systems were investigated at 900, 1000, 1100 and 1300 °C. Electron probe microanalysis was used to determine ...
Thermodynamic Description of the Ti-Al-O System Based on Experimental Data
Phase equilibria of the TiO2-Al2O3 system were investigated experimentally using XRD, SEM/EDX and DTA methods. Temperature stability limits of the aluminum titanate (Al2TiO5) were detected. The thermodynamic parameters of ...