The net added fraction of thermally-generated atomic sites, ΔNN, has been measured, during equilibrium heating to near the melting point, in a coarse-grained copper bar of 99.999% purity. The linear thermal expansion, ΔLL, ...

The adiabatic elastic constants C44, 1/2(Cll-C12), and 1/2(cll+C12+2c44) have been measured for copper, silver, and gold over the temperature range from 300° to about BOO 0K using the conventional ultrasonic pulse-echo ...

Measurements of change in length and change in lattice parameter were made at identical temperatures on 99.995% aluminum in the temperature range 229 to 656°C. Length changes, ΔL, were measured on an unconstrained horizontal ...

Measurements of the elastic moduli of aluminum over the temperature range 300°–930°K are reported. These data together with those reported for T < 300°K, show that all elastic moduli, including the shear moduli, vary ...

The annealing kinetics of voids in 99.9999 wt% pure aluminum were studied over the temperature range 85 to 209 °C in thin specimens by transmission electron microscopy. The isothermal shrinkage of individual voids was ...

Supporting technical data sheets, MSDS, surface pretreatment and bonding processes, travel sheets, and mode-of-failure surveys

An adhesively bonded single lap joint was used to study the effects of coupon thickness, bondline thickness, surface preparation, presence of an overflow fillet, and adhesive type. Gains in the Education of Mathematics and ...

A three-dimensional grain map of an investment-cast, open-cell, aluminum foam is generated using a combination of experimentally derived and synthetically derived data. Specifically, the experimental data are derived from ...